Superconductivity at 38 K in Iron-Based Compound with Platinum-Arsenide Layers Ca10(Pt4As8)(Fe2-xPtxAs2)5

We report superconductivity in novel iron-based compounds Ca10(PtnAs8)(Fe2-xPtxAs2)5 with n = 3 and 4. Both compounds crystallize in triclinic structures (space group P-1), in which Fe2As2 layers alternate with PtnAs8 spacer layers. Superconductivity with a transition temperature of 38 K is observed in the n = 4 compound with a Pt content of x ~ 0.36 in the Fe2As2 layers. The compound with n = 3 exhibits superconductivity at 13 K.Comment: OPEN SELECT article, 11 pages, 5 figures, 2 table

Pressure Dependence of Superconducting Transition Temperature on Perovskite-Type Fe-Based Superconductors and NMR Study of Sr2VFeAsO3

We report the pressure dependences of the superconducting transition temperature (T_c) in several perovskite-type Fe-based superconductors through the resistivity measurements up to ~4 GPa. In Ca_4(Mg,Ti)_3Fe_2As_2O_y with the highest T_c of 47 K in the present study, the T_c keeps almost constant up to ~1 GPa, and starts to decrease above it. From the comparison among several systems, we obtained a tendency that low T_c with the longer a-axis length at ambient pressure increases under pressure, but high T_c with the shorter a-axis length at ambient pressure hardly increases. We also report the ^75As-NMR results on Sr_2VFeAsO_3. NMR spectrum suggests that the magnetic ordering occurs at low temperatures accompanied by some inhomogeneity. In the superconducting state, we confirmed the anomaly by the occurrence of superconductivity in the nuclear spin lattice relaxation rate 1/T_1, but the spin fluctuations unrelated with the superconductivity are dominant. It is conjectured that the localized V-3d moments are magnetically ordered and their electrons do not contribute largely to the Fermi surface and the superconductivity in Sr_2VFeAsO_3.Comment: 7 pages, 9 figure

Structural Features of Layered Iron Pnictide Oxides (Fe2As2)(Sr4M2O6)

Structural features of newly found perovskite-based iron pnictide oxide system have been systematically studied. Compared to REFePnO system, perovskite-based system tend to have lower Pn-Fe-Pn angle and higher pnictogen height owing to low electronegativity of alkaline earth metal and small repulsive force between pnictogen and oxygen atoms. As-Fe-As angles of (Fe2As2)(Sr4Cr2O6), (Fe2As2)(Sr4V2O6) and (Fe2Pn2)(Sr4MgTiO6) are close to ideal tetrahedron and those pnictogen heights of about 1.40 A are close to NdFeAsO with optimized carrier concentration. These structural features of this system may leads to realization of high Tc superconductivity.Comment: 3pages, 2figures, 1table, proceedings of M2S 200

Effects of metallic spacer in layered superconducting Sr2(Mgy_yTi1−y_{1-y})O3FeAs

The highly two-dimensional superconducting system Sr2(Mg$_y$Ti$_{1-y}$)O3FeAs, recently synthesized in the range of 0.2 < y < 0.5, shows an Mg concentration-dependent $T_c$. Reducing the Mg concentration from y=0.5 leads to a sudden increase in $T_c$, with a maximum $T_c$ ~40 K at y=0.2. Using first principles calculations, the unsynthesized stoichiometric y=0 and the substoichiometric y=0.5 compounds have been investigated. For the 50% Mg-doped phase (y=0.5), Sr2(Mg$_y$Ti$_{1-y}$)O3 layers are completely insulating spacers between FeAs layers, leading to the fermiology such as that found for other Fe pnictides. At y=0, representing a phase with metallic Sr2TiO3 layers, the $\Gamma$-centered Fe-derived Fermi surfaces (FSs) considerably shrink or disappear. Instead, three $\Gamma$-centered Ti FSs appear, and in particular two of them have similar size, like in MgB2. Interestingly, FSs have very low Fermi velocity in large fractions: the lowest being 0.6$\times10^6$ cm/s. Furthermore, our fixed spin moment calculations suggest the possibility of magnetic ordering, with magnetic Ti and nearly nonmagnetic Fe ions. These results indicate a crucial role of Sr2(Mg$_y$Ti$_{1-y}$)O3 layers in this superconductivity.Comment: 7 pages; Proceedings of ICSM-201

A New Iron Pnictide Oxide (Fe2As2)(Ca5(Mg,Ti)4Oy) and a New Phase in Fe-As-Ca-Mg-Ti-O system

A new layered iron arsenide oxide (Fe2As2)(Ca5(Mg,Ti)4Oy) and its structural derivative were found in the Fe-As-Ca-Mg-Ti-O system. The crystal structure of (Fe2As2)(Ca5(Mg,Ti)4Oy) is identical to that of (Fe2As2)(Ca5(Sc,Ti)4Oy), which was reported in our previous study. The lattice constants of this compound are a = 3.86(4) A and c = 41.05(2) A. In addition, another phase with a thicker blocking layer was found. The structure of the compound and its derivative was tentatively assigned through STEM observation as (Fe2As2)(Ca8(Mg,Ti)6Oy) with sextuple perovskite-type sheets divided by a rock salt layer. The interlayer Fe-Fe distance of this compound is ~30 A. The compound and its derivative exhibited bulk superconductivity, as found from magnetization and resistivity measurements.Comment: 9 pages, 7 figure

Lung Rest During Extracorporeal Membrane Oxygenation for Neonatal Respiratory Failure-Practice Variations and Outcomes.

OBJECTIVE: Describe practice variations in ventilator strategies used for lung rest during extracorporeal membrane oxygenation for respiratory failure in neonates, and assess the potential impact of various lung rest strategies on the duration of extracorporeal membrane oxygenation and the duration of mechanical ventilation after decannulation. DATA SOURCES: Retrospective cohort analysis from the Extracorporeal Life Support Organization registry database during the years 2008-2013. STUDY SELECTION: All extracorporeal membrane oxygenation runs for infants less than or equal to 30 days of life for pulmonary reasons were included. DATA EXTRACTION: Ventilator type and ventilator settings used for lung rest at 24 hours after extracorporeal membrane oxygenation initiation were obtained. DATA SYNTHESIS: A total of 3,040 cases met inclusion criteria. Conventional mechanical ventilation was used for lung rest in 88% of cases and high frequency ventilation was used in 12%. In the conventional mechanical ventilation group, 32% used positive end-expiratory pressure strategy of 4-6 cm H2O (low), 22% used 7-9 cm H2O (mid), and 43% used 10-12 cm H2O (high). High frequency ventilation was associated with an increased mean (SEM) hours of extracorporeal membrane oxygenation (150.2 [0.05] vs 125 [0.02]; p \u3c 0.001) and an increased mean (SEM) hours of mechanical ventilation after decannulation (135 [0.09] vs 100.2 [0.03]; p = 0.002), compared with conventional mechanical ventilation among survivors. Within the conventional mechanical ventilation group, use of higher positive end-expiratory pressure was associated with a decreased mean (SEM) hours of extracorporeal membrane oxygenation (high vs low: 136 [1.06] vs 156 [1.06], p = 0.001; mid vs low: 141 [1.06] vs 156 [1.06]; p = 0.04) but increased duration of mechanical ventilation after decannulation in the high positive end-expiratory pressure group compared with low positive end-expiratory pressure (p = 0.04) among survivors. CONCLUSIONS: Wide practice variation exists with regard to ventilator settings used for lung rest during neonatal respiratory extracorporeal membrane oxygenation. Use of high frequency ventilation when compared with conventional mechanical ventilation and use of low positive end-expiratory pressure strategy when compared with mid positive end-expiratory pressure and high positive end-expiratory pressure strategy is associated with longer duration of extracorporeal membrane oxygenation. Further research to provide evidence to drive optimization of pulmonary management during neonatal respiratory extracorporeal membrane oxygenation is warranted

Evidence for Nodal superconductivity in Sr2_{2}ScFePO3_{3}

Point contact Andreev reflection spectra have been taken as a function of temperature and magnetic field on the polycrystalline form of the newly discovered iron-based superconductor Sr2ScFePO3. A zero bias conductance peak which disappears at the superconducting transition temperature, dominates all of the spectra. Data taken in high magnetic fields show that this feature survives until 7T at 2K and a flattening of the feature is observed in some contacts. Here we inspect whether these observations can be interpreted within a d-wave, or nodal order parameter framework which would be consistent with the recent theoretical model where the height of the P in the Fe-P-Fe plane is key to the symmetry of the superconductivity. However, in polycrystalline samples care must be taken when examining Andreev spectra to eliminate or take into account artefacts associated with the possible effects of Josephson junctions and random alignment of grains.Comment: Published versio

Contrasting Pressure Effects in Sr2VFeAsO3 and Sr2ScFePO3

We report the resistivity measurements under pressure of two Fe-based superconductors with a thick perovskite oxide layer, Sr2VFeAsO3 and Sr2ScFePO3. The superconducting transition temperature Tc of Sr2VFeAsO3 markedly increases with increasing pressure. Its onset value, which was Tc{onset}=36.4 K at ambient pressure, increases to Tc{onset}=46.0 K at ~4 GPa, ensuring the potential of the "21113" system as a high-Tc material. However, the superconductivity of Sr2ScFePO3 is strongly suppressed under pressure. The Tc{onset} of ~16 K decreases to ~5 K at ~4 GPa, and the zero-resistance state is almost lost. We discuss the factor that induces this contrasting pressure effect.Comment: 5 pages, 4 figures, to be published in J. Phys. Soc. Jpn. No.12 (2009

Superconductivity in Ti-doped Iron-Arsenide Compound Sr4Cr0.8Ti1.2O6Fe2As2

Superconductivity was achieved in Ti-doped iron-arsenide compound Sr4Cr0.8Ti1.2O6Fe2As2 (abbreviated as Cr-FeAs-42622). The x-ray diffraction measurement shows that this material has a layered structure with the space group of \emph{P4/nmm}, and with the lattice constants a = b = 3.9003 A and c = 15.8376 A. Clear diamagnetic signals in ac susceptibility data and zero-resistance in resistivity data were detected at about 6 K, confirming the occurrence of bulk superconductivity. Meanwhile we observed a superconducting transition in the resistive data with the onset transition temperature at 29.2 K, which may be induced by the nonuniform distribution of the Cr/Ti content in the FeAs-42622 phase, or due to some other minority phase.Comment: 3 pages, 3 figure